[Chang, Long]

We’ll try the arc-spray coating from Pentagon Technologies and keep the other advice in mind.  Thanks everyone!

--Long
On Oct 12, 2016, at 3:33 PM, Gerhard Ulbricht <ulbricht at physics.ucsb.edu<mailto:ulbricht at physics.ucsb.edu>> wrote:

Sputtering at lower power will produce less heat and thermal stress and can delay flaking, but flakes will still show up when the film deposited on your sputter chimney and shutter gets thicker.

What we do for materials that are very prone to flaking (e.g. RF sputtered Si or DC sputtered W) is to send out chimney and shutter to get their insides arc-spray coated with a very rough and thick Al layer - about the surface structure of extra coarse sand paper. That for us has stopped Si flaking completely, in contrast to having to clean the sputter gun from flakes every 2 weeks. We have to get these parts re-coated every time we change a sputter target, but the company (Pentagon Technologies) does both the bead blasting and the new coating for us (what is very convenient), and it's not expensive.

Best regards,

Gerhard Ulbricht
Department of Physics
Broida Hall
University of California
Santa Barbara CA 93106



On 10/11/2016 4:24 PM, Chang, Long wrote:
Hi All,

We have a DC magnetron sputtering system using 2” diameter targets.  We’ve been observing many shorts due to severe flaking.  The student is using a recipe developed by her predecessor which uses 100W of DC power and 5 mTorr of Ar.  Does anyone know what steps should be taken to avoid/reduce flaking when DC sputtering ITO?  I suspect that the student is using too much power.

Thanks,
Long Chang
Nanofab Manager
University of Houston
3605 Cullen Blvd, Entrance 14
Room E1007A, SERC Bldg 545
Houston, TX 77204-5062




_______________________________________________
labnetwork mailing list
labnetwork at mtl.mit.edu<mailto:labnetwork at mtl.mit.edu>
https://www-mtl.mit.edu/mailman/listinfo.cgi/labnetwork



-------------- next part --------------
An HTML attachment was scrubbed...
URL: <https://mtl.mit.edu/pipermail/labnetwork/attachments/20161012/f9f99c6a/attachment.html>